International Journal of Pharmaceutical Investigation, 2012, 2, 2, 70-77.
DOI: 10.4103/2230-973X.100040
Published: August 2012
Type: Original Article
Authors:
Gaurav Khurana
Chitkara College of Pharmacy, Chandigarh-Patiala National Highway, Rajpura-140401, Patiala, Punjab, India.
Sandeep Arora
Chitkara College of Pharmacy, Chandigarh-Patiala National Highway, Rajpura-140401, Patiala, Punjab, India.
Pravin K Pawar
Chitkara College of Pharmacy, Chandigarh-Patiala National Highway, Rajpura-140401, Patiala, Punjab, India.
ABSTRACT
Background: Many polymeric systems have been used to fabricate ocular inserts for improve ocular bioavailability and retention to drug of which matrix systems have shown advantages of reduce dosing frequency and increased corneal residence time. The objective of the present investigation was to prepare and evaluate ocular inserts of gatifloxacin. Materials and Methods: Ocular insert was made from an aqueous dispersion of gatifloxacin, sodium alginate, polyvinyl alcohol, and glycerin by solvent casting method. Ocular insert (5.5 mm) was cross-linked by CaCl2 and was coated with Eudragit RL-100 or Eudragit RS-100. The ocular inserts were characterized for thickness; uniformity of weight, drug content uniformity, % moisture absorption or moisture loss, and surface pH. The in vitro diffusion studies were carried out by putting insert on Millipore membrane filter (0.8 μm) fixed between donor and receptor compartment of an all glass modified Franz diffusion cell. Results: The thickness and drug content of ocular insert were found in the range of 0.11 ± 0.003 to 0.24 ± 0.010 mm and 0.718 ± 0.002 to 0.867 ± 0.007 mg, respectively. The surface pH, % moisture absorption or moisture loss and weight variation values were obtained in satisfactory range. The crosslinked ocular insert coated with Eudragit RL-100 shows maximum drug permeation i.e. 89.53 % ± 0.43 at 11 h. The stability studies suggest that all ocular insert remained stable, showed lesser degradation rate and maximum shelf life. Conclusion: Ocular inserts of gatifloxacin were prepared successfully by using solvent casting method for sustained drug delivery. The cross-linked and Eudragit RL-100 coated ocular insert of gatifloxacin provides better in vitro drug release and sustained upto 11 h.
Keywords: Cross-linked, Gatifloxacin, Ocular insert, Polyvinyl Alcohol, Sodium alginate.